Elastollan® C60AW
热塑性聚氨酯弹性体(聚酯)
BASF Corp. Thermoplastic Polyurethanes
产品说明:
Elastollan® C60AW is a polyester-based thermoplastic polyurethane (TPU) containing a plasticizer. It exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C60AW is supplied uncolored in pellet form.
Elastollan® C60AW 物性表附加功能
基本信息
添加剂 | |
特性 | 抗溶剂性 良好的撕裂强度 良好耐磨损性 耐热性,高 韧性良好 水解稳定
|
外观 | |
加工方法 | |
物理性能额定值单位制测试方法
比重 | 1.14 | g/cm³ | ASTM D792 |
熔流率(熔体流动速率) (190°C/3.8 kg) | 20 到 60 | g/10 min | ASTM D1238 |
硬度额定值单位制测试方法
肖氏硬度 (邵氏 A) | 61 |
| ASTM D2240 |
机械性能额定值单位制测试方法
拉伸模量 (注塑) | 5.52 | MPa | ASTM D412 |
弯曲模量 (注塑) | 8.96 | MPa | ASTM D790 |
泰伯耐磨性 | 40.0 | mg | ASTM D1044 |
Abrasion - DIN | 20 | mm³ | DIN 53516 |
热性能额定值单位制测试方法
Softening Point - DMA | 109 | °C | 内部方法 |
弹性体额定值单位制测试方法
拉伸应力 |
|
| ASTM D412 |
应变 | 3.65 | MPa | ASTM D412 |
300%应变 | 8.96 | MPa | ASTM D412 |
抗张强度 | 23.4 | MPa | ASTM D412 |
伸长率 (断裂) | 760 | % | ASTM D412 |
撕裂强度 1 | 64.8 | kN/m | ASTM D624 |
压缩变形 |
|
| ASTM D395B |
23°C, 22 hr | 20 | % | ASTM D395B |
70°C, 22 hr | 45 | % | ASTM D395B |
热性能额定值单位制测试方法
玻璃转化温度 | -52.0 | °C | 内部方法 |
维卡软化温度 | 66.0 | °C | ASTM D1525 |
注射额定值单位制
建议的大水分含量 | 0.030 | % |
|
料筒后部温度 | 170 到 210 | °C |
|
料筒中部温度 | 170 到 210 | °C |
|
料筒前部温度 | 170 到 210 | °C |
|
射嘴温度 | 200 到 210 | °C |
|
挤出额定值单位制
料筒1区温度 | 140 到 175 | °C |
|
料筒3区温度 | 140 到 175 | °C |
|
料筒5区温度 | 140 到 175 | °C |
|
接头温度 | 160 到 175 | °C |
|
口模温度 | 165 到 170 | °C |
|