Hostaform® S 9364 WS 10/1570
聚甲醛（POM）共聚物
Celanese Corporation
产品说明：
Preliminary Data Sheet
Hostaform® acetal copolymer grade S 9364 WS 10/1570 is a highly impact modified grade for demanding applications that also need improved resistance to UV exposure. Besides weatherability, Hostaform® S 9364 WS 10/1570 provides a significant improvement in impact strength and flexibility over standard impact modified grades such as Hostaform® S 9063 and S 9064. This grade is only available in black.
Chemical abbreviation according to ISO 1043-1: POM-HI
Hostaform® S 9364 WS 10/1570 物性表附加功能
基本信息
| 添加剂 | |
| 特性 | 冲击改性 抗撞击性，良好 良好的柔韧性 耐气候影响性能良好
|
| RoHS 合规性 | |
| 外观 | |
| 树脂ID (ISO 1043) | |
物理性能额定值单位制测试方法
| 密度 | 1.37 | g/cm³ | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 4.50 | cm³/10min | ISO 1133 |
| 吸水率 (饱和, 23°C) | 0.80 | % | ISO 62 |
机械性能额定值单位制测试方法
| 拉伸模量 | 1500 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 41.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 20 | % | ISO 527-2/1A/50 |
| 弯曲模量 (23°C) | 1400 | MPa | ISO 178 |
冲击性能额定值单位制测试方法
| 简支梁缺口冲击强度 |
|
| ISO 179/1eA |
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 16 | kJ/m² | ISO 179/1eA |
热性能额定值单位制测试方法
| 热变形温度 (1.8 MPa, 未退火) | 75.0 | °C | ISO 75-2/A |
| 熔融温度 1 | 166 | °C | ISO 11357-3 |
| 线形热膨胀系数 |
|
| ISO 11359-2 |
| 流动 | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| 横向 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
注射额定值单位制
| 干燥温度 | 80.0 到 100 | °C |
|
| 干燥时间 | 3.0 | hr |
|
| 料筒后部温度 | 170 到 180 | °C |
|
| 料筒中部温度 | 180 到 190 | °C |
|
| 料筒前部温度 | 180 到 190 | °C |
|
| 射嘴温度 | 180 到 200 | °C |
|
| 加工（熔体）温度 | 180 到 200 | °C |
|
| 模具温度 | 60.0 到 70.0 | °C |
|
| 注塑压力 | 60.0 到 120 | MPa |
|
| 注射速度 | 慢 |
|
|
| 保压 | 60.0 到 120 | MPa |
|
| 背压 | 0.00 到 0.500 | MPa |
|
注射说明
| Zone 4 Temperature: 180 to 200°C |