Hostaform® C 13031 K聚甲醛(POM)共聚物白垩填料Celanese Corporation产品说明:
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 04-002, K5
POM copolymer
Easy flowing Injection molding type with higher strength, rigidity
and hardness with special chalk modified; good chemical resistance
to solvents, fuel and strong alkalis as well as good hydrolysis
resistance; high resistance to thermal and oxidative degradation;
good wear properties
UL-registration in natural and a thickness more than 1.5 mm as UL 94
HB.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: For unlubricated or once-only-lubricant
sliding Parts and gear wheels.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
附加功能
黄卡编号 | E42337-234599 |
填料/增强材料 | 白垩填料 |
特性 | 刚性,高 高强度 抗溶剂性 流动性中等 耐化学性良好 耐碱 耐磨损性良好 耐燃油性 耐水解性 |
用途 | 车轮 齿轮 |
RoHS 合规性 | 联系制造商 |
树脂ID (ISO 1043) | POM |
Hostaform® C 13031 K 物性表
密度 | 1.44 | g/cm³ | ISO 1183 |
溶化体积流率(MVR) (190°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
收缩率 | ISO 294-4 | ||
垂直流动方向 | 1.8 | % | ISO 294-4 |
流动方向 | 2.0 | % | ISO 294-4 |
吸水率 (饱和, 23°C) | 0.65 | % | ISO 62 |
拉伸模量 | 3100 | MPa | ISO 527-2/1A/1 |
拉伸应力 (屈服) | 64.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 (屈服) | 8.0 | % | ISO 527-2/1A/50 |
标称拉伸断裂应变 | 15 | % | ISO 527-2/1A/50 |
简支梁缺口冲击强度 | ISO 179/1eA | ||
-30°C | 5.0 | kJ/m² | ISO 179/1eA |
23°C | 5.0 | kJ/m² | ISO 179/1eA |
热变形温度 (1.8 MPa, 未退火) | 105 | °C | ISO 75-2/A |
熔融温度 1 | 170 | °C | ISO 11357-3 |
线形热膨胀系数 - 流动 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
表面电阻率 | 1.0E+14 | ohms | IEC 60093 |
体积电阻率 | 1.0E+14 | ohms·cm | IEC 60093 |
介电强度 | 35 | kV/mm | IEC 60243-1 |
相对电容率 | IEC 60250 | ||
100 Hz | 4.20 | IEC 60250 | |
1 MHz | 4.20 | IEC 60250 | |
耗散因数 | IEC 60250 | ||
100 Hz | 2.5E-3 | IEC 60250 | |
1 MHz | 8.0E-3 | IEC 60250 | |
漏电起痕指数 | 600 | V | IEC 60112 |
UL 阻燃等级 | UL 94 | ||
1.50 mm | HB | UL 94 | |
3.00 mm | HB | UL 94 |
干燥温度 | 100 到 120 | °C | |
干燥时间 | 3.0 到 4.0 | hr | |
建议的大水分含量 | 0.15 | % | |
料斗温度 | 20.0 到 30.0 | °C | |
料筒后部温度 | 170 到 180 | °C | |
料筒中部温度 | 180 到 190 | °C | |
料筒前部温度 | 190 到 200 | °C | |
射嘴温度 | 190 到 210 | °C | |
加工(熔体)温度 | 190 到 210 | °C | |
模具温度 | 80.0 到 120 | °C | |
注塑压力 | 60.0 到 120 | MPa | |
注射速度 | 慢 | ||
保压 | 60.0 到 120 | MPa | |
背压 | 0.00 到 2.00 | MPa |
- 抗冲击POM Hostaform® S 9364 WS 10/1570 2024-06-16
- POM Hostaform® C 9021 M 含二硫化钼润滑剂 2024-06-16
- 现货抗静电POM C 27021 AST/泰科纳 2024-06-16
- 现货POM Hostaform® C 27021 赫斯特代理商 2024-06-16
- 导电 碳纤增强POM Tenac™-C CF452 日本旭化成 2024-06-16
- 高刚性POM 日本旭化成 GN455 赛钢料 2024-06-16
- 现货抗翘曲 POM 旭化成 Tenac™ 5050 2024-06-16
- POM Hostaform® C 9021 K 耐碱 耐燃油 2024-06-16
- 现货POM美国杜邦 1700P 聚甲醛 2024-06-16
- 高韧性POM Hostaform® C 13021 2024-06-16